A two pack high build epoxy Polyamide based under coat containing inert pigments. It is recommended as a final coat in an Epoxy system.
High build in single coat.
Excellent resistance to fresh and salt water
Abrasion resistance and flexible films.
Excellent inter-coat adhesion.
Resistant to solvents.
Resistance to mild acids.
Coating for long term protection for structural steel, concrete surface and internal lining of edible oil tanks, and fuel tanks. Suitable for marine installations, power plants, fertilizers, hospitals, laboratories, etc.
Colour : As per Shade Card
Finish : Smooth/Glossy, Semi Gloss
Specific gravity : 1.40±0.05 when mixed A+B
Volume of Solids : 55±2%
Theoretical Coverage13:5-9.5 m2/lit
Recommended (D.F.T.) : 35-55 Microns/Coat
Recommended (W.F.T.) : 70-100 Microns/Coat
Flash point : 25 ° C (ISO 367 –83)
Surface Dry : 4-6 hrs
Hard Dry : 10-12 hrs.
Min. 12 hrs.
Max. 7 days
Pot life : 8 hours at 25 ° C
Mixing ratio : 4 parts base"A":1 part hardner "B"
Solvent : Epoxy thinner.
High temperature will accelerate dry times and decrease pot life; lower temperature will lengthen cure times and slightly increase pot life. Normally Tollens Epoxy primer grey A+B mixing pot life is 8hrs.As a diluents using Tollens Epoxy thinner 10– 15 %.
Tollens Epoxy Primer can be brushed, rolled or sprayed. . Use where application temperature can be proceed above 4 ° C
Brush, Roller or Spray.
Epoxy top-coat is recommended as a final coat in an Epoxy system. Surface preparation is pre conditioned for an optimum performance of the system. The surface to be top coated must be free from all surface contaminates like dust, dirt grease or any other contaminates. If the previous epoxy coat is more than 15 days cured at 35oC, single coat of epoxy tie coat is recommended to achieve proper inter-coat adhesion.
10-15 % depending on the method of application.
Tollens Epoxy Thinner.
Tip – 2200 PSI / 0.015" – 0.020"
Atomizing pressure: 40 PSI
Metal drums 5 US gallons
18months, in original sealed container, with proper storage.
1 St Coat | 2 nd Coat | 3 rd Coat | Total D.F.T (u) | |
---|---|---|---|---|
Marine | Epoxy ZP | Epoxy HB Undercoat | Epoxy HB Top Coat | 350-375 |
Edible oil tanks & fuel tanks | Epoxy HB ZP | Epoxy HB Undercoat | Epoxy HB Top Coat | 300-350 |
Pipe lines | Epoxy Red Oxide Primer | Epoxy HB Undercoat | Epoxy HB Top Coat | 300-300 |
General/ Maintenance | EpoxyRed Oxide Primer | Epoxy HB Undercoat | Epoxy HB Top Coat | 250-250 |
Concrete and Plaster | Epoxy HB Primer | Epoxy HB Undercoat | Epoxy HB Top Coat | 300-350 |